HIC-550 / HT-9234 High Temperature Iron Filled Casting System

SKU: HIC-550 / HT-9234. Category: .

RATIO
100 pbw to 10 pbw

GENERAL DESCRIPTION
HIC-550 is an iron filled two component, high temperature, epoxy casting system. This system has excellent physical properties at elevated temperatures, for casting molds used in producing parts.

RECOMMENDED POST CURE

  • 1 hour at 100°F
  • 1 hour at 150°F
  • 1 hour at 200°F
  • 1 hour at 250°F
  • 1 hour at 300°F
  • 2 hours at 350°F
  • 1 hour at 300°F
  • 1 hour at 250°F
  • 1 hour at 200°F
  • 1 hour at 150°F
  • 1 hour at 100°F

After oven has cooled to ambient temperature, tool can be removed.

HARDENER SELECTION

HT-8433
60 minute pot life; shorter pot life for smaller casting

HT-9234
140 minute pot life; long pot life for larger casting.

HT-8401
30 hours pot life; Longer pot life for larger mass castings.

Additional Information

Ratio By Weight

100 pbw to 10 pbw

Ratio By Volume

5.7 to 1

Pot Life (400 Gram Mass)

140 Minutes

Hardness, Shore "D" (at 72°F)

88

Hardness, Shore 'D" (at 350°F)

79

Density: Mixed

14.03

Viscosity: Mixed

67,800 cps

Shelf Life: Resin/Hardener

1 Year